Filament Barrus PA-CX12 For 3D Printers

PLN129.27 tax excl.
PLN159.00 tax incl.

Filament Barrus PA-CX12 is a high quality polyamide material based on PA12 nylon.

Filament Barrus PA-CX12 is a high performance industrial nylon. It is durable and flexible and at the same time resistant to hitting, abrasion, cracking and scratches. The material is resistant to chemicals and UV rays. Has low moisture absorption.

Diameter
  • 2,85mm
Color
  • White
  • Black
  • Colorless
Quantity
Out of stock


  • Security Policy Security Policy
  • Delivery policy Delivery policy
  • Return Policy Return Policy

Filament Barrus PA-CX12

is a high quality polyamide material based on PA12 nylon.
Filament Barrus PA-CX12 is a high performance industrial nylon. It is durable and flexible and at the same time resistant to hitting, abrasion, cracking and scratches. The material is resistant to chemicals and UV rays. Has low moisture absorption.

Barrus PA-CX12 is a filament with a wide range of applications. This material is resistant to bending and scratching. Provides high impact resistance and resistance to chemicals and weather conditions. Food contact is possible. It has excellent dimensional stability. Perfect for semi-professional prints, it provides the perfect combination between print ease and model durability

Barus PA-CX12 requires a heated table. The recommended temperature is 80 ° C - 100 ° C or even more. It can be used in all printers that work in FDM / FFF technology. Filament does not stick well to clean glass, therefore additional adhesives are required. To achieve the best results, it is recommended to dry the material in air dryers for a few hours before printing.

The material should be stored in a dry and cool place (15 ° C - 25 ° C) sealed with a moisture absorber and protected against UV rays.

Data sheet

Weight
500 g
Print temperature
240° - 260°C
Table temperature
80 - 100°C
Heated working table
Yes
Filament diameter
2,85mm
Tensile strength
Test method: ISO 527 1/2 Typical value: 60 MPa
Strain at Break
Test method: ISO 527 1/2 Typical value: more than 150%
Tensile modulus
Test method: ISO 527 Typical value: 1400 MPa
Impact strength - Izod method 23°C
Test method: ISO 179 Typical value: 14 KJ / m2
Melting temperature
Test method: ISO 11357 Typical value: 250 ° C +/- 10 ° C
Specific gravity
Test method: ISO 1183 Typical value: 1.02 g / cc
Viscosity (relative to PA12)
Test method: ISO 307 Typical value: 170 ± 10 cm3 / g
Shore'a D hardness
Test method: ISO 868 Typical value: 81
HDT 264 psi.annealed
Test method: ISO 75-2 / A Typical value: 105 ° C

Data sheet

Weight
500 g
Print temperature
240° - 260°C
Table temperature
80 - 100°C
Heated working table
Yes
Filament diameter
2,85mm
Tensile strength
Test method: ISO 527 1/2 Typical value: 60 MPa
Strain at Break
Test method: ISO 527 1/2 Typical value: more than 150%
Tensile modulus
Test method: ISO 527 Typical value: 1400 MPa
Impact strength - Izod method 23°C
Test method: ISO 179 Typical value: 14 KJ / m2
Melting temperature
Test method: ISO 11357 Typical value: 250 ° C +/- 10 ° C
Specific gravity
Test method: ISO 1183 Typical value: 1.02 g / cc
Viscosity (relative to PA12)
Test method: ISO 307 Typical value: 170 ± 10 cm3 / g
Shore'a D hardness
Test method: ISO 868 Typical value: 81
HDT 264 psi.annealed
Test method: ISO 75-2 / A Typical value: 105 ° C