Filament Barrus TPU98A For 3D Printers

PLN96.75 tax excl.
PLN119.00 tax incl.

Filament Barrus TPU98A is a high quality, flexible material produced in the Netherlands. It is packed on a foil wrapped in a box with a window.

Barrus TPU98A is a flexible material designed for easy and quick printing in both direct feeders and Bowden tubes

Diameter
  • 1,75mm
  • 2,85mm
Color
  • Colorless
Quantity
Out of stock


  • Security Policy Security Policy
  • Delivery policy Delivery policy
  • Return Policy Return Policy

Filament Barrus TPU98A

is a high quality, flexible material produced in the Netherlands. It is packed on a foil wrapped in a box with a window.

Barrus TPU98A is a flexible material designed for easy and quick printing in both direct feeders and Bowden tubes.

Barrus TPU98A it is a flexible material, designed for easy and quick printing in both direct feeders and Bowden tubes. Filament is resistant to high temperature (up to 138 ° C) and allows stretching up to 450% before it breaks. It can be printed on a clean fast and does not require a heated table. For printers with a heated table, the recommended temperature is max. 60 ° C. It provides easy printing, excellent adhesion and high mechanical strength. You can print at a speed greater than 75mm / s. It is resistant to oils and greases and is waterproof. Suitable for printers with FDM / FFF technology.

The material should be stored in a dry and cool place, protected from UV rays.

Data sheet

Weight
500 g
Print temperature
225°C – 250°C
Heated working table
No
Filament diameter
1,75 mm / 2,85 mm
Filament type
Flexible Flex/TPU
Specific gravity
Test method: ISO 1183 Typical value: 1.16 g / cc
Tensile strength
Test method: ISO 527 1/2 Typical value: 50 MPa
Strain at Break
Test method: ISO 527 1/2 Typical value: 450%
Melting temperature
220°C +/- 10°C
Shore'a D hardness
Test method: ISO 7619-1 Typical value: 98A
Glass transition
Test method: DSC Typical value: - 16 ° C
Vicat
Test method: ASTM D 1525 Typical value: 138 ° C

Data sheet

Weight
500 g
Print temperature
225°C – 250°C
Heated working table
No
Filament diameter
1,75 mm / 2,85 mm
Filament type
Flexible Flex/TPU
Specific gravity
Test method: ISO 1183 Typical value: 1.16 g / cc
Tensile strength
Test method: ISO 527 1/2 Typical value: 50 MPa
Strain at Break
Test method: ISO 527 1/2 Typical value: 450%
Melting temperature
220°C +/- 10°C
Shore'a D hardness
Test method: ISO 7619-1 Typical value: 98A
Glass transition
Test method: DSC Typical value: - 16 ° C
Vicat
Test method: ASTM D 1525 Typical value: 138 ° C