Filament Barrus CARBON For 3D Printers

PLN104.88 tax excl.
PLN129.00 tax incl.

The Barrus CARBON filament is a strong and durable PET-G material with 20% carbon fiber. This material is 2x more durable than PET-G and more resistant to impact and temperature (up to 80 ° C).

The Barrus CARBON filament is the perfect material for many applications. It has a matt surface, no shrinkage, dimensional stability and ease of printing. It is used, among others: RC models, drones, car parts.

Diameter
  • 1,75mm
  • 2,85mm
Color
  • Black
Quantity
Product available with different options


  • Security Policy Security Policy
  • Delivery policy Delivery policy
  • Return Policy Return Policy

Filament Barrus CARBON

it is a strong and durable PET-G material with 20% addition of carbon fibers. This material is 2x more durable than PET-G and more resistant to impact and temperature (up to 80 ° C).

Filament Barrus CARBON it's the perfect material for many applications. It has a matt surface, no shrinkage, dimensional stability and ease of printing. It is used, among others: RC models, drones, car parts. The CARBON is extremely rigid with increased durability and temperature resistance. It is an abrasive filament. Can be used in printers without a heated table. For heated table printers, the recommended temperature is 35 ° C - 60 ° C. It can be used in printers working in FDM / FFF technology.

The Barrus CARBON filament adheres well to the glass. Due to their abrasive properties, they should be printed with hardened nozzles, eg steel or titanium nozzles. Ordinary brass nozzles may be subject to accelerated wear.

The material should be stored in a dry and cool place protected from UV rays.

Data sheet

Weight
500 g
Print temperature
220° - 250°C
Heated working table
No
Filament diameter
1,75 mm / 2,85 mm
Tensile strength
Test method : ISO 527 Typical value : 39 MPa
Strain at Break
Test method: ISO 527 Typical value: 8.0%
Impact strength - Izod method 23°C
Test method: ISO 180-1A Typical value: 3.8 kJ / m2
Melting temperature
225°C - 245°C
Specific gravity
Test method: ASTM D792 Typical value: 1.19 g / cc
MFI 300°C, 1,2 kg
Test method: ISO 1133 Typical value: ND
HDT
Test method: ASTM D648 Typical value: 80 ° C

Data sheet

Weight
500 g
Print temperature
220° - 250°C
Heated working table
No
Filament diameter
1,75 mm / 2,85 mm
Tensile strength
Test method : ISO 527 Typical value : 39 MPa
Strain at Break
Test method: ISO 527 Typical value: 8.0%
Impact strength - Izod method 23°C
Test method: ISO 180-1A Typical value: 3.8 kJ / m2
Melting temperature
225°C - 245°C
Specific gravity
Test method: ASTM D792 Typical value: 1.19 g / cc
MFI 300°C, 1,2 kg
Test method: ISO 1133 Typical value: ND
HDT
Test method: ASTM D648 Typical value: 80 ° C