Filament Barrus METAL Brass For 3D Printers

zł117.89 tax excl.
zł145.00 tax incl.

Filament Barrus METAL Brass is an easy to print material based on PLA with the addition of 70% brass. The material has abrasive properties, therefore it is recommended to print with hardened nozzles.

Diameter
  • 1,75mm
  • 2,85mm
Color
  • Brass
Quantity
Last items in stock

Filament Barrus METAL Brass it is easy to print material based on PLA with the addition of 70% brass. The material has abrasive properties, therefore it is recommended to print with hardened nozzles.

Filament Barrus METAL Brass it can be used in printers without a heated table. For table top printers it is recommended that the temperature is up to 35 ° C - 60 ° C.

The material should be stored in a dry and cool place protected from UV rays.

Barrus METAL Brass in its composition has 70% brass, it is easy to print and later polishing. Allows you to print metal-like objects. It is 2.2 x heavier than PLA and gives a metal surface and thermal conductivity. It does not shrink during printing. It enables printing on almost every printer working in FDM technology due to the appropriate hardness. The printer should have a nozzle with a diameter greater than 0.35 mm. Due to the abrasion caused by the high content of metal, it is recommended to use hardened nozzles

Data sheet

Print temperature
185°C - 195°C
Heated working table
No
Filament diameter
1,75 mm / 2,85 mm
Filament type
Brass
Melting temperature
Test method: ISO 294 Typical value: 195 ° C +/- 10 ° C
Vicat softening temperature
Test method: ISO 306 Typical value: +/- 65 °C
Specific gravity
Test method: ISO 1183 Typical value: 2.78 g / cc
Weight
750 g

Data sheet

Print temperature
185°C - 195°C
Heated working table
No
Filament diameter
1,75 mm / 2,85 mm
Filament type
Brass
Melting temperature
Test method: ISO 294 Typical value: 195 ° C +/- 10 ° C
Vicat softening temperature
Test method: ISO 306 Typical value: +/- 65 °C
Specific gravity
Test method: ISO 1183 Typical value: 2.78 g / cc
Weight
750 g